Chemically strengthenable lithium aluminosilicate glasses with inherent damage resistance

ABSTRACT

A group of glass compositions in the Li 2 O—Al 2 O 3 —SiO 2 —B 2 O 3  family that can be chemically strengthened in single or multiple ion exchange baths containing at least one of NaNO 3  and KNO 3  for a short time (2-4 hours) to develop a deep depth of layer (DOL). In some instances, the DOL is at least 70 μm; in others, at least about 100 μm. The ion exchanged glasses have a high damage resistance (indentation fracture toughness ranging form greater than 10 kgf to greater than 50 kgf) that is better than or at least comparable to that of sodium aluminosilicate glasses.

CROSS-REFERENCE TO RELATED APPLICATIONS

This application is a continuation of and claims the benefit of priority under 35 U.S.C. § 120 to U.S. application Ser. No. 17/522,221 filed on Nov. 9, 2021, which is a continuation of and claims the benefit of priority under 35 U.S.C. § 120 to U.S. application Ser. No. 16/193,266, filed Nov. 16, 2018, now U.S. Pat. No. 11,220,452, issued Jan. 11, 2022, which is a divisional of and claims the benefit of priority under 35 U.S.C. § 121 to U.S. application Ser. No. 15/400,267, filed Jan. 6, 2017, now U.S. Pat. No. 10,131,567, issued Nov. 20, 2018, which claims the benefit of priority under 35 U.S.C. § 119 of U.S. Provisional Application Ser. No. 62/276,431, filed Jan. 8, 2016, the contents of each of which are relied upon and incorporated herein by reference in their entirety.

BACKGROUND

The disclosure relates to ion exchangeable glasses. More particularly, the disclosure relates to ion exchangeable lithium aluminosilicate glasses. Even more particularly, the disclosure relates to lithium aluminosilicate glasses which, when ion exchanged, have high levels of inherent damage resistance.

There have been continuous efforts in the development of new glass compositions to improve ion exchange properties and higher damage resistance while facilitating melting and forming processes. Many glasses with high indentation threshold are based on the SiO₂—Al₂O₃—B₂O₃—MgO—Na₂O—P₂O₅ glass systems. The open structure (i.e. high molar volume) resulting from the existence of boron or phosphorus leads to high inherent damage resistance (IDR).

SUMMARY

A group of glass compositions in the Li₂O—Al₂O₃—SiO₂—B₂O₃ family is provided. These glasses can be chemically strengthened in single or multiple ion exchange baths containing at least one of NaNO₃ and KNO₃ for a short time (2-4 hours) to develop a deep depth of layer (DOL). In some instances, the DOL is at least 70 μm; in others, at least about 100 μm. The ion exchanged glasses have a high damage resistance (indentation fracture toughness ranging from greater than 10 kgf to greater than 50 kgf) that is better than or at least comparable to that of sodium aluminosilicate glasses.

Accordingly, one aspect of the disclosure is to provide a lithium aluminosilicate glass. The glass comprises: from about 55 mol % to about 75 mol % SiO₂; from about 9 mol % to about 18 mol % Al₂O₃; from about 2.5 mol % to about 20 mol % B₂O₃; from about 3 mol % to about 20 mol % Li₂O; and from 0 mol % to about 4 mol % P₂O₅.

Another aspect of the disclosure is to provide a lithium aluminosilicate glass. The glass is ion exchanged and has a compressive layer extending to a depth of layer of at least about 70 μm from at least one surface into the glass. The compressive layer having a maximum compressive stress at the surface of at least about 600 MPa. The glass also has a Vickers crack initiation threshold of at least about 10 kgf and a Knoop scratch threshold of at least about 8 N.

According to a first aspect of the disclosure a lithium aluminosilicate glass is provided. The lithium aluminosilicate glass comprises: from about 55 mol % to about 75 mol % SiO₂; from about 10 mol % to about 18 mol % Al₂O₃; from about 3.5 mol % to about 9.5 mol % B₂O₃; from about 7 mol % to about 14 mol % Li₂O; and from 0 mol % to about 4 mol % P₂O₅, wherein Li₂O (mol %)/R₂O (mol %) is in a range from about 0.1 to about 0.4 and R₂O=Li₂O+Na₂O+K₂O+Rb₂O+Cs₂O.

According to a second aspect of the disclosure, the lithium aluminosilicate glass of the first aspect is ion exchanged.

According to a third aspect of the disclosure, the ion exchanged lithium aluminosilicate glass of the second aspect has a compressive layer extending to a depth of layer of at least about 70 μm from at least one surface into the glass, the compressive layer having a maximum compressive stress of at least about 600 MPa.

According to a fourth aspect of the disclosure, in the ion exchanged lithium aluminosilicate glass of the third aspect the compressive layer has a compressive stress of at least about 100 MPa at a depth of 50 μm below the surface.

According to a fifth aspect of the disclosure, the ion exchanged lithium aluminosilicate glass of any of the second through fourth aspects has a Vickers crack initiation threshold of at least about 10 kgf.

According to a sixth aspect of the disclosure, the ion exchanged lithium aluminosilicate glass of any of the second through fifth aspects has a Knoop scratch threshold of at least about 8 N.

According to a seventh aspect of the disclosure, the lithium aluminosilicate glass of any of the first through sixth aspects has a liquidus viscosity of at least about 10 kP.

According to an eighth aspect of the disclosure, the lithium aluminosilicate glass of any of the first through seventh aspects has a softening point of about 840° C. or less.

According to a ninth aspect of the disclosure, the lithium aluminosilicate glass of any of the first through eighth aspects has an anneal point of at least about 510° C.

According to a tenth aspect of the disclosure, the lithium aluminosilicate glass of any of the first through ninth aspects has an elastic modulus of at least about 68 GPa.

According to an eleventh aspect of the disclosure, the lithium aluminosilicate glass of any of the first through tenth aspects is provided wherein R₂O (mol %)-Al₂O₃ (mol %) is in a range from about −2 mol % to about 5.6 mol %.

According to a twelfth aspect of the disclosure, the lithium aluminosilicate glass of any of the first through eleventh aspects is provided wherein Al₂O₃ (mol %)>B₂O₃ (mol %).

According to a thirteenth aspect of the disclosure, the lithium aluminosilicate glass of any of the first through twelfth aspects is provided wherein the lithium aluminosilicate glass comprises: from about 58 mol % to about 69 mol % SiO₂; from about 10 mol % to about 17 mol % Al₂O₃; from about 3.5 mol % to about 9.5 mol % B₂O₃; from 0 mol % to about 2.5 mol % P₂O₅; from about 7 mol % to about 14 mol % Li₂O; from about 0.2 mol % to about 14 mol % Na₂O; from 0 mol % to about 2.5 mol % K₂O; from 0 mol % to about 5 mol % MgO; and from 0 mol % to about 4 mol % ZnO, wherein Li₂O (mol %)/R₂O (mol %) is in a range from about 0.1 to about 0.4.

According to a fourteenth aspect of the disclosure, the lithium aluminosilicate glass of any of the first through thirteenth aspects is provided wherein the lithium aluminosilicate glass comprises: from about 5 mol % to about 9 mol % B₂O₃; from about 7 mol % to about 10 mol % Li₂O; from about 4 mol % to about 14 mol % Na₂O; and from 0 mol % to about 1 mol % K₂O.

According to a fifteenth aspect of the disclosure, the lithium aluminosilicate glass of any of the first through fourteenth aspects is provided wherein (Al₂O₃ (mol %)+B₂O₃ (mol %))/R₂O (mol %) is in a range from about 0.9 to about 1.9.

According to a sixteenth aspect of the disclosure, the lithium aluminosilicate glass of any of the first through fifteenth aspects is provided wherein R₂O (mol %)+R′O (mol %)−Al₂O₃ (mol %)−B₂O₃ (mol %)−P₂O₅ (mol %) is in a range from about −10.5 mol % to about −0.11 mol %, where R′O=MgO+CaO+SrO+BaO.

According to a seventeenth aspect of the disclosure, the lithium aluminosilicate glass of any of the first through sixteenth aspects is provided wherein the lithium aluminosilicate glass comprises from about 5 mol % to about 12 mol % Li₂O.

According to an eighteenth aspect of the disclosure, the lithium aluminosilicate glass of any of the first through seventeenth aspects is provided wherein the lithium aluminosilicate glass comprises: from 0 mol % to about 5 mol % Na₂O; from 0 mol % to about 4 mol % K₂O; from 0 mol % to about 8 mol % MgO; from 0 mol % to about 4 mol % ZnO; from 0 mol % to about 5 mol % TiO₂; and from 0 mol % to about 3 mol % P₂O₅.

According to a nineteenth aspect of the disclosure, the lithium aluminosilicate glass of any of the first through eighteenth aspects is provided wherein the lithium aluminosilicate glass comprises: from about 55 mol % to about 60 mol % SiO₂; from about 12 mol % to about 15 mol % Al₂O₃; from about 3.5 mol % to about 7.5 mol % B₂O₃; from about 7 mol % to about 10 mol % Li₂O; and from 0 mol % to about 3 mol % P₂O₅.

According to a twentieth aspect of the disclosure, the lithium aluminosilicate glass of any of the first through nineteenth aspects is provided wherein the lithium aluminosilicate glass comprises from about 5 mol % to about 7 mol % B₂O₃.

According to a twenty-first aspect of the disclosure, the lithium aluminosilicate glass of any of the first through twentieth aspects is provided wherein the lithium aluminosilicate glass comprises: from 0 mol % to about 5 mol % Na₂O; and from about 0.05 mol % to about 0.5 mol % SnO₂.

According to a twenty-second aspect of the disclosure a consumer electronic product is provided. The consumer electronic product comprises: a housing having a front surface, a back surface and side surfaces; electrical components provided at least partially within the housing, the electrical components including at least a controller, a memory, and a display, the display being provided at or adjacent the front surface of the housing; and a cover glass disposed over the display, wherein at least one of a portion of the housing or the cover glass comprises the lithium aluminosilicate glass of any of the first through twenty-first aspects.

According to a twenty-third aspect of the disclosure a consumer electronic product is provided. The lithium aluminosilicate glass comprises: from about 55 mol % to about 75 mol % SiO₂; from about 10 mol % to about 18 mol % Al₂O₃; from about 2.5 mol % to about 7.5 mol % B₂O₃; from about 5 mol % to about 14 mol % Li₂O; from 0 mol % to about 4 mol % P₂O₅; and from 0 mol % to about 1 mol % K₂O; wherein Li₂O (mol %)/R₂O (mol %) is in a range from about 0.1 to about 0.4, R₂O=Li₂O+Na₂O+K₂O+Rb₂O+Cs₂O, R₂O (mol %)+R′O (mol %)−Al₂O₃ (mol %)−B₂O₃ (mol %)−P₂O₅ (mol %) is in a range from about −10.5 mol % to about −0.11 mol %, and R′O=MgO+CaO+SrO+BaO.

According to a twenty-fourth aspect of the disclosure, the lithium aluminosilicate glass of the twenty-third aspect is ion exchanged.

According to a twenty-fifth aspect of the disclosure, the ion exchanged lithium aluminosilicate glass of the twenty-fourth aspect has a compressive layer extending to a depth of layer of at least about 70 μm from at least one surface into the glass, the compressive layer having a maximum compressive stress of at least about 600 MPa.

According to a twenty-sixth aspect of the disclosure, in the ion exchanged lithium aluminosilicate glass of the twenty-fifth aspect the compressive layer has a compressive stress of at least about 100 MPa at a depth of 50 μm below the surface.

According to a twenty-seventh aspect of the disclosure, the lithium aluminosilicate glass of any of the twenty-third through twenty-sixth aspects has a Vickers crack initiation threshold of at least about 10 kgf.

According to a twenty-eighth aspect of the disclosure, the lithium aluminosilicate glass of any of the twenty-third through twenty-seventh aspects has a Knoop scratch threshold of at least about 8 N.

According to a twenty-ninth aspect of the disclosure, the lithium aluminosilicate glass of any of the twenty-third through twenty-eighth aspects has a liquidus viscosity of at least about 10 kP.

According to a thirtieth aspect of the disclosure, the lithium aluminosilicate glass of any of the twenty-third through twenty-ninth aspects has a softening point of about 840° C. or less.

According to a thirty-first aspect of the disclosure, the lithium aluminosilicate glass of any of the twenty-third through thirtieth aspects has an anneal point of at least about 510° C.

According to a thirty-second aspect of the disclosure, the lithium aluminosilicate glass of any of the twenty-third through thirty-first aspects has an elastic modulus of at least about 68 GPa.

According to a thirty-third aspect of the disclosure, the lithium aluminosilicate glass of any of the twenty-third through thirty-second aspects is provided wherein R₂O (mol %)-Al₂O₃ (mol %) is in a range from about −2 mol % to about 5.6 mol %.

According to a thirty-fourth aspect of the disclosure, the lithium aluminosilicate glass of any of the twenty-third through thirty-third aspects is provided wherein Al₂O₃ (mol %)>B₂O₃ (mol %).

According to a thirty-fifth aspect of the disclosure, the lithium aluminosilicate glass of any of the twenty-third through thirty-fourth aspects is provided wherein (Al₂O₃ (mol %)+B₂O₃ (mol %))/R₂O (mol %) is in a range from about 0.9 to about 1.9.

According to a thirty-sixth aspect of the disclosure, the lithium aluminosilicate glass of any of the twenty-third through thirty-fifth aspects is provided wherein the lithium aluminosilicate glass comprises: from 0 mol % to about 5 mol % Na₂O; from 0 mol % to about 8 mol % MgO; from 0 mol % to about 4 mol % ZnO; from 0 mol % to about 5 mol % TiO₂; and from 0 mol % to about 3 mol % P₂O₅.

According to a thirty-seventh aspect of the disclosure, the lithium aluminosilicate glass of any of the twenty-third through thirty-sixth aspects is provided wherein the lithium aluminosilicate glass comprises from about 5 mol % to about 7 mol % B₂O₃.

According to a thirty-eighth aspect of the disclosure, the lithium aluminosilicate glass of any of the twenty-third through thirty-seventh aspects is provided wherein the lithium aluminosilicate glass comprises: from 0 mol % to about 5 mol % Na₂O; and from about 0.05 mol % to about 0.5 mol % SnO₂.

According to a thirty-ninth aspect of the disclosure a consumer electronic product is provided. The consumer electronic product comprises: a housing having a front surface, a back surface and side surfaces; electrical components provided at least partially within the housing, the electrical components including at least a controller, a memory, and a display, the display being provided at or adjacent the front surface of the housing; and a cover glass disposed over the display, wherein at least one of a portion of the housing or the cover glass comprises the lithium aluminosilicate glass of any of the twenty-third through thirty-eighth aspects.

According to a fortieth aspect of the disclosure a lithium aluminosilicate glass is provided. The lithium aluminosilicate glass is ion exchanged and has a compressive layer extending to a depth of layer of at least about 70 μm from at least one surface into the glass, the compressive layer having a maximum compressive stress of at least about 600 MPa, wherein the glass has a Vickers crack initiation threshold of at least about 10 kgf and a Knoop scratch threshold of at least about 8 N.

According to a forty-first aspect of the disclosure a consumer electronic product is provided. The consumer electronic product comprises: a housing having a front surface, a back surface and side surfaces; electrical components provided at least partially within the housing, the electrical components including at least a controller, a memory, and a display, the display being provided at or adjacent the front surface of the housing; and a cover glass disposed over the display, wherein at least one of a portion of the housing or the cover glass comprises the lithium aluminosilicate glass of the fortieth aspect.

These and other aspects, advantages, and salient features of the present disclosure will become apparent from the following detailed description, the accompanying drawings, and the appended claims.

BRIEF DESCRIPTION OF THE DRAWINGS

FIG. 1 is a cross-sectional schematic view of an ion exchanged glass article;

FIG. 2 is a plot of Na⁺ concentration profile from the surface of the glass to the inner portion of the glass for a lithium aluminosilicate glass of the present disclosure (A) and a glass ceramic (B);

FIG. 3 is a plot of indentation fracture threshold for a lithium aluminosilicate glass of the present disclosure, ion exchanged at 390° C. in NaNO₃ for 3.5 hours, and sodium aluminosilicate glasses after ion exchange in KNO₃;

FIG. 4 shows optical microscopic images of Vickers indentations in the ion exchanged lithium aluminosilicate glass plotted in FIG. 3 under indenter loads of 10 kgf, 30 kgf, and 50 kgf;

FIG. 5A is a plan view of an exemplary electronic device incorporating any of the articles disclosed herein; and

FIG. 5B is a perspective view of the exemplary electronic device of FIG. 5A.

DETAILED DESCRIPTION

In the following description, like reference characters designate like or corresponding parts throughout the several views shown in the figures. It is also understood that, unless otherwise specified, terms such as “top,” “bottom,” “outward,” “inward,” and the like are words of convenience and are not to be construed as limiting terms. In addition, whenever a group is described as comprising at least one of a group of elements and combinations thereof, it is understood that the group may comprise, consist essentially of, or consist of any number of those elements recited, either individually or in combination with each other. Similarly, whenever a group is described as consisting of at least one of a group of elements or combinations thereof, it is understood that the group may consist of any number of those elements recited, either individually or in combination with each other. Unless otherwise specified, a range of values, when recited, includes both the upper and lower limits of the range as well as any ranges therebetween. As used herein, the indefinite articles “a,” “an,” and the corresponding definite article “the” mean “at least one” or “one or more,” unless otherwise specified. It also is understood that the various features disclosed in the specification and the drawings can be used in any and all combinations.

As used herein, the terms “glass article” and “glass articles” are used in their broadest sense to include any object made wholly or partly of glass. Unless otherwise specified, all compositions are expressed in terms of mole percent (mol %). Coefficients of thermal expansion (CTE) are expressed in terms of 10⁻⁷/° C. and represent a value measured over a temperature range from about 20° C. to about 300° C., unless otherwise specified.

Unless otherwise specified, all temperatures are expressed in terms of degrees Celsius (° C.). As used herein the term “softening point” refers to the temperature at which the viscosity of a glass is approximately 10^(7.6) poise (P), the term “anneal point” refers to the temperature at which the viscosity of a glass is approximately 10^(13.2) poise, the term “200 poise temperature (T^(200P))” refers to the temperature at which the viscosity of a glass is approximately 200 poise, the term “1 poise temperature (T^(200P))” refers to the temperature at which the viscosity of a glass is approximately 200 poise, the term “10¹¹ poise temperature” refers to the temperature at which the viscosity of a glass is approximately 10¹¹ poise, the term “35 kP temperature (T^(35P))” refers to the temperature at which the viscosity of a glass is approximately 35 kilopoise (kP), and the term “160 kP temperature (T^(160kP))” refers to the temperature at which the viscosity of a glass is approximately 160 kP. As used herein, the term “liquidus temperature,” or “T^(L)” refers to the temperature at which crystals first appear as a molten glass cools down from the melting temperature, or the temperature at which the very last crystals melt away as temperature is increased from room temperature.

It is noted that the terms “substantially” and “about” may be utilized herein to represent the inherent degree of uncertainty that may be attributed to any quantitative comparison, value, measurement, or other representation. These terms are also utilized herein to represent the degree by which a quantitative representation may vary from a stated reference without resulting in a change in the basic function of the subject matter at issue. Thus, a glass that is “substantially free of MgO” is one in which MgO is not actively added or batched into the glass, but may be present in very small amounts (e.g., less than 0.1 mol %) as a contaminant.

Referring to the drawings in general and to FIG. 1 in particular, it will be understood that the illustrations are for the purpose of describing particular embodiments and are not intended to limit the disclosure or appended claims thereto. The drawings are not necessarily to scale, and certain features and certain views of the drawings may be shown exaggerated in scale or in schematic in the interest of clarity and conciseness.

Described herein are ion exchangeable lithium aluminosilicate glasses that exhibit high levels of damage resistance—also referred to as native damage resistance or inherent damage resistance—as characterized by Vickers crack initiation threshold and Knoop scratch testing, when chemically strengthened. These glasses may in general be ion exchanged in sodium salts (e.g., NaNO₃) at faster rates than analogous sodium alkali aluminosilicate glasses are ion exchanged in potassium salts (e.g., KNO₃). Deeper depths of compression (also referred to as “depth of layer” or “DOL”) may also be achieved at lower temperatures with the lithium-containing glasses. When Na+ replaces Li+ in the glass, the rate of diffusion may be about 10 times faster than exchange of K⁺ for Na⁺ in the glass. Mixed salt baths may be used to allow for dual ion exchange in which both K⁺ for Na⁺ and Na⁺ for Li⁺ exchange occur, resulting in a deep depth of compression due to the Na⁺ for Li⁺ exchange and high surface compressive stress due to the K⁺ for Na⁺ exchange.

The lithium aluminosilicate glasses described herein comprise or consist essentially of: from about 55 mol % to about 75 mol % SiO₂ (55 mol %≤SiO₂≤75 mol %); from about 9 mol % to about 18 mol % Al₂O₃ (9 mol %≤Al₂O₃≤18 mol %); from about 2.5 mol % to about 20 mol % B₂O₃ (2.5 mol %≤B₂O₃≤20 mol %); from about 3 mol % to about 20 mol % Li₂O (3 mol %≤Li₂O≤20 mol %); and from 0 mol % to about 4 mol % P₂O₅ (0 mol %≤P₂O₅≤4 mol %). In some embodiments, the glass further comprises at least one of: from 0 mol % to about 5 mol % Na₂O; from 0 mol % to about 4 mol % K₂O; from 0 mol % to about 8 mol % MgO; from 0 mol % to about 4 mol % ZnO, and from 0 mol % to about 5 mol % TiO₂.

In particular embodiments, the lithium aluminosilicate glasses described herein comprise or consist essentially of: from about 55 mol % to about 75 mol % SiO₂; from about 10 mol % to about 18 mol % Al₂O₃; from 0 mol % to about 20 mol % B₂O₃; from about 5 mol % to about 14 mol % Li₂O; from 0 mol % to about 5 mol % Na₂O; from 0 mol % to about 4 mol % K₂O; from 0 mol % to about 8 mol % MgO; from 0 mol % to about 4 mol % ZnO; from 0 mol % to about 5 mol % TiO₂; from 0 mol % to about 4 mol % P₂O₅, and from about 0.05 mol % to about 0.5 mol % SnO₂. Even more particularly, the glass may comprise or consist essentially of: from about 55 mol % to about 60 mol % SiO₂ (55 mol %≤SiO₂≤60 mol %); from about 12 mol % to about 15 mol % Al₂O₃ (12 mol %≤Al₂O₃≤15 mol %); from about 2.5 mol % to about 7.5 mol % B₂O₃ (2.5 mol %≤B₂O₃≤7.5 mol %); from about 7 mol % to about 10 mol % Li₂O (7 mol %≤Li₂O≤10 mol %); and from 0 mol % to about 3 mol % P₂O₅ (0 mol %≤P₂O₅≤3 mol %). Most preferably, B₂O₃ is in a range from about 5 mol % to about 7 mol %. Non-limiting examples of the compositions of such glasses and a reference composition (9667) are listed in Table 1.

TABLE 1 Examples of the lithium aluminosilicate glasses. mol % Reference 1 2 3 4 5 oxide 9667 REN REO RET RGC RDD SiO₂ 69.2 65.0 63.0 59.3 63.3 67.3 Al₂O₃ 12.6 14.4 15.5 15.4 15.3 13.5 B₂O₃ 1.8 2.3 2.3 6.0 6.0 2.0 Li₂O 7.7 8.8 9.7 9.7 9.6 7.7 Na₂O 0.4 0.6 0.6 0.6 0.6 0.6 MgO 2.9 4.0 4.0 4.0 4.0 4.0 ZnO 1 .7 1.2 1.2 1.2 1.2 1.2 TiO₂ 3.5 3.5 3.5 3.6 0.0 3.5 SnO₂ 0.2 0.2 0.2 0.2 0.2 0.2 P₂O₅ 0 0 0 0 0 0 mol % 6 7 8 9 10 11 oxide RDE RDF RDG RDH RDI RFX SiO₂ 65.9 64.7 63.4 62.3 61.0 68.9 Al₂O₃ 13.2 13.0 12.7 12.5 12.2 13.9 B₂O₃ 4.0 5.8 7.6 9.2 10.9 2.4 Li₂O 7.5 7.5 7.3 7.1 7.1 7.9 Na₂O 0.6 0.6 0.6 0.6 0.5 0.6 MgO 4.0 3.8 3.8 3.7 3.7 4.1 ZnO 1.2 1.1 1.1 1.1 1.1 1.2 TiO₂ 3.4 3.4 3.3 3.3 3.2 0 SnO₂ 0.2 0.2 0.2 0.2 0.2 0.1 P₂O₅ 0 0 0 0 0 0.9 mol % 12 13 14 15 oxide RFY RFZ RGA RGB SiO₂ 68.2 67.6 66.9 69.5 Al₂O₃ 13.8 13.6 13.5 14.0 B₂O₃ 2.3 2.3 2.3 2.4 Li₂O 7.9 7.8 7.7 8.0 Na₂O 0.6 0.6 1.7 0.6 MgO 4.0 4.0 4.0 4.1 ZnO 1.2 1.2 1.2 1.2 TiO₂ 0 0 0 0 SnO₂ 0.1 0.1 0.1 0.1 P₂O₅ 1.8 2.7 2.7 0.0

In particular embodiments, the lithium aluminosilicate glasses described herein comprise or consist essentially of: from about 58 mol % to about 69 mol % SiO₂ (58 mol %≤SiO₂≤69 mol %); from about 9 mol % to about 17 mol % Al₂O₃ (9 mol %≤Al₂O₃≤17 mol %); from about 3.5 mol % to about 9.5 mol % B₂O₃ (3.5 mol %≤B₂O₃≤9.5 mol %); from 0 mol % to about 2.5 mol % P₂O₅ (0 mol %≤P₂O₅≤4 mol %); from about 2.5 mol % to about 12 mol % Li₂O (2.5 mol %≤Li₂O≤12 mol %); from about 0.2 mol % to about 12 mol % Na₂O (0.2 mol %≤Na₂O≤13 mol %); from 0 mol % to about 2.5 mol % K₂O (0 mol %≤K₂O≤2.5 mol %); 0 mol % to about 5 mol % MgO (0 mol %≤MgO≤5 mol %); and/or from 0 mol % to about 4 mol % ZnO (0 mol %≤ZnO≤4 mol %). More particularly, the glass may comprise: from about 5 mol % to about 9 mol % B₂O₃ (5 mol %≤B₂O₃≤9 mol %); from about 4 mol % to about 10 mol % Li₂O (4 mol %≤Li₂O≤10 mol %); from about 4 mol % to about 14 mol % Na₂O (4 mol %≤Na₂O≤14 mol %); from 0 mol % to about 1 mol % K₂O (0 mol %≤K₂O≤1 mol %); 0 mol % to about 3 mol % MgO (0 mol %≤MgO≤3 mol %); and/or from 0 mol % to about 3 mol % ZnO (0 mol %≤ZnO≤3 mol %). These glasses may further include from about 0.05 mol % to about 0.5 mol % SnO₂ (0.05 mol %≤SnO₂≤0.5 mol %). Non-limiting examples of the compositions of such glasses are listed in Table 2.

In some embodiments, (Li₂O (mol %)/R₂O (mol %) is in a range from about 0.1 to about 0.5 (0.1≤(Li₂O (mol %)/R₂O (mol %)≤0.5), where R₂O=Li₂O+Na₂O+K₂O+Rb₂O+Cs₂O.

In some embodiments, R₂O (mol %)-Al₂O₃ (mol %) is in a range from about −2 mol % to about 5.6 mol %, where R₂O=Li₂O+Na₂O+K₂O+Rb₂O+Cs₂O. In some embodiments, Al₂O₃ (mol %)>B₂O₃ (mol %). In some embodiments, (Al₂O₃ (mol %)+B₂O₃ (mol %))/R₂O (mol %) is in a range from about 0.9 to about 1.9. In some embodiments, R₂O (mol %)+R′O (mol %)−Al₂O₃ (mol %)−B₂O₃ (mol %)−P₂O₅ (mol %) is in a range from about −10.5 mol % to about −0.11 mol %, where R′O=MgO+CaO+SrO+BaO.

In some embodiments, the lithium aluminosilicate glasses described herein have softening points that are lower than sodium analogs, which typically have softening points of greater than about 900° C. In some embodiments, the glasses described herein have softening points of about 840° C. or less. In certain embodiments, the glass has a softening point of about 820° C. or less and, in still other embodiments, about 800° C. or less. These low softening points are accompanied by coefficients of thermal expansion (CTE) that are lower than those of sodium analogs. Lower CTE is important in maintaining dimensional stability when reforming glass sheets. In addition to use as flat plates, the relatively low CTEs of the present glasses enable their use as three-dimensional articles and in automotive applications.

In some embodiments, the lithium aluminosilicate glasses described herein have an anneal point of at least about 500° C. In certain embodiments the glass has an anneal point of at least about 520° C. and, in still other embodiments, the anneal point is at least about 530° C.

Densities, strain points, softening points, anneal points, and coefficients of thermal expansion (CTE) for selected glass compositions are listed in Table 2.

TABLE 2 Compositions, densities, strain points, softening points, anneal points, and coefficients of thermal expansion (CTE) of selected lithium aluminosilicate glasses. mol % 196HNT 107UE 107UF 107UG 107UH 107UI SiO₂ 67.00 67.11 67.18 66.96 67.17 67.20 Al2O₃ 12.60 9.14 10.12 9.13 10.15 10.15 B₂O₃ 7.10 0.00 0.00 0.00 0.00 0.00 Li₂O 5.10 8.10 7.66 6.28 5.24 5.23 Na₂O 6.70 11.38 10.86 13.26 13.27 13.31 K₂O 1.30 0.26 0.27 0.26 0.26 0.27 MgO 1.17 1.08 1.29 1.12 1.75 CaO 1.82 1.82 1.80 1.78 1.09 SnO₂ 0.10 0.00 0.00 0.00 0.00 0.00 R₂O—Al₂O₃ 0.50 Li₂O/(R₂O) 0.389 0.410 0.408 0.317 0.279 0.278 Strain Pt. 459.1 473.2 462.8 482.3 482.3 (° C.) Anneal Pt. 500.2 514.1 504.5 525.6 524.9 (° C.) Softening Pt. 691.8 719.3 703.8 733 739.7 (° C.) CTE 87.8 84.2 89.9 86.9 87 (×10⁻⁷/° C.) Density 2.474 2.471 2.479 2.477 2.473 (g/cm³) mol % 107UJ 107UK 107UL 107UM 107UN 107UO SiO₂ 67.01 70.21 70.17 70.14 71.17 71.19 Al2O₃ 10.14 8.51 8.50 8.49 7.47 6.88 B₂O₃ 0.00 0.00 0.00 0.00 0.00 0.00 Li₂O 6.30 5.45 6.49 6.93 5.33 5.28 Na₂O 11.32 11.30 10.32 9.82 11.49 12.09 K₂O 0.27 0.98 0.99 0.99 0.99 0.98 MgO 2.15 1.02 0.99 1.06 1.02 1.04 CaO 1.80 1.53 1.53 1.55 1.53 1.52 SnO₂ 0.00 0.00 0.00 0.00 0.00 0.00 R₂O—Al₂O₃ Li₂O/(R₂O) 0.352 0.307 0.365 0.391 0.299 0.288 Strain Pt. 485.5 469.2 466.8 464.2 460.5 452.8 (° C.) Anneal Pt. 529 511.6 509.5 506.9 502.3 495.3 (° C.) Softening Pt. 741 728.6 720.1 714.1 712.3 702.7 (° C.) CTE 83.3 84.2 83.1 82.4 84.5 85.3 (×10⁻⁷/° C.) Density 2.474 2.458 2.455 2.453 2.454 2.452 (g/cm³) mol % 107UP 107UQ 107UR 107US 107UT 107UU SiO₂ 69.60 66.42 66.49 66.27 66.33 65.31 Al2O₃ 7.78 9.39 9.38 8.09 8.09 6.98 B₂O₃ 0.00 0.00 0.00 0.00 0.00 0.00 Li₂O 5.10 6.39 6.37 11.73 10.66 9.65 Na₂O 12.90 11.57 11.60 9.98 9.97 10.48 K₂O 0.98 1.23 1.23 0.01 0.01 1.49 MgO 1.08 0.05 0.04 0.03 0.04 0.51 CaO 1.55 3.55 2.51 1.05 2.08 2.59 SnO₂ 0.00 0.00 0.00 0.00 0.00 0.00 R₂O—Al₂O₃ Li₂O/(R₂O) 0.269 0.333 0.332 0.540 0.516 0.446 Strain Pt. 452.6 474.5 484 460.6 466.7 452.7 (° C.) Anneal Pt. 494.2 515.5 526.7 499.5 506.9 492.3 (° C.) Softening Pt. 697 711.3 732.2 693.2 697.6 678.6 (° C.) CTE 90.5 90.1 87.6 86.7 84.9 92.5 (×10⁻⁷/° C.) Density 2.468 2.499 2.519 2.51 2.519 2.539 (g/cm³) mol % 107UV 107UW 107UX 107UY 107UZ 107VA SiO₂ 65.28 65.86 67.91 69.80 68.09 67.98 Al2O₃ 6.96 9.56 8.99 8.49 10.01 10.99 B₂O₃ 0.00 0.00 0.00 0.00 0.00 0.00 Li₂O 9.67 8.42 7.96 7.40 6.77 5.91 Na₂O 10.49 11.70 10.94 10.36 10.96 10.94 K₂O 2.48 0.27 0.27 0.24 0.25 0.27 MgO 0.03 1.09 1.03 0.98 1.02 1.02 CaO 2.07 1.90 1.79 1.69 1.78 1.78 SnO₂ 0.00 0.11 0.10 0.09 0.10 0.10 R₂O—Al₂O₃ Li₂O/(R₂O) 0.427 0.413 0.415 0.411 0.376 0.345 Strain Pt. 448.3 464 464 469 484 503 (° C.) Anneal Pt. 486.2 505 506 511 526 548 (° C.) Softening Pt. 671.5 697 706 716 737 772 (° C.) CTE 84.2 90.4 86.7 86.3 83.8 82 (×10⁻⁷/° C.) Density 2.537 2.485 2.472 2.458 2.47 2.468 (g/cm³) mol % 107VB 107VC 107VD 107VE 107VF 107VG SiO₂ 67.98 67.26 66.04 65.24 66.39 66.15 Al2O₃ 9.00 9.43 9.95 10.46 8.99 10.98 B₂O₃ 0.00 0.00 0.00 0.00 0.00 0.00 Li₂O 7.92 7.78 7.82 7.77 7.56 7.76 Na₂O 10.96 11.39 11.96 12.37 11.94 11.93 K₂O 0.26 0.26 0.27 0.26 0.26 0.27 MgO 1.34 1.00 1.04 1.01 1.00 1.03 CaO 1.42 1.78 1.82 1.77 1.77 1.78 SnO₂ 0.10 0.10 0.10 0.10 0.10 0.10 R₂O—Al₂O₃ Li₂O/(R₂O) 0.414 0.400 0.390 0.381 0.382 0.389 Strain Pt. 466 463 465 468 470 460 (° C.) Anneal Pt. 508 505 506 508 512 501 (° C.) Softening Pt. 707 706 702 706 712 697 (° C.) CTE 86.3 86.7 89.4 89.4 88.3 89.7 (×10⁻⁷/° C.) Density 2.469 2.401 2.407 2.432 2.411 2.38 (g/cm³) mol % 107VH 107VI 107VJ 107VK 107VL 107VM SiO₂ 65.17 65.52 64.53 63.51 62.63 61.19 Al2O₃ 9.96 5.11 6.46 7.71 9.04 10.39 B₂O₃ 0.00 0.00 0.00 0.00 0.00 0.00 Li₂O 7.73 12.67 11.95 11.23 10.52 10.05 Na₂O 11.94 12.40 12.78 13.29 13.59 14.13 K₂O 0.27 0.27 0.27 0.27 0.26 0.27 MgO 1.78 1.05 1.05 1.04 1.03 1.04 CaO 2.04 1.85 1.83 1.84 1.80 1.81 SnO₂ 0.10 0.10 0.10 0.10 0.10 0.10 R₂O—Al₂O₃ Li₂O/(R₂O) 0.388 0.500 0.478 0.453 0.432 0.411 Strain Pt. 465 412 416 426 435 443 (° C.) Anneal Pt. 506 447 453 462 471 481 (° C.) Softening Pt. 701 602 616 626 640 655 (° C.) CTE 90.1 105.9 104.8 103.5 103.3 101.7 (×10⁻⁷/° C.) Density 2.413 2.485 2.49 2.495 2.499 2.511 (g/cm³) mol % 107VN 107VU 107VW 107VX 107VY 107VZ SiO₂ 60.07 68.95 66.00 66.12 68.85 68.81 Al2O₃ 11.72 9.97 9.96 9.98 9.96 9.94 B₂O₃ 0.00 0.00 0.00 0.00 0.00 0.00 Li₂O 9.21 7.96 5.00 4.99 7.98 9.94 Na₂O 14.75 4.94 7.90 7.90 4.96 2.98 K₂O 0.26 0.99 0.99 0.99 0.99 1.01 MgO 1.06 3.57 3.59 3.50 5.10 2.04 CaO 1.82 1.54 1.53 1.52 2.05 5.17 SnO₂ 0.10 0.09 0.10 0.09 0.10 0.10 R₂O—Al₂O₃ Li₂O/(R₂O) 0.380 0.573 0.360 0.359 0.573 0.714 Strain Pt. 452 546.8 524.5 566.4 511.7 500.4 (° C.) Anneal Pt. 492 592.6 570.9 611.2 556.4 541.5 (° C.) Softening Pt. 672 825 812.3 830.7 N/A N/A (° C.) CTE 103.1 65.1 74.5 69.4 67.4 66.1 (×10⁻⁷/° C.) Density 2.506 2.478 2.493 2.531 2.434 2.445 (g/cm³) mol % 107WA 107WB 107WC 107WD 107WE 107WF SiO₂ 68.91 66.92 66.84 68.7 68.63 67.85 Al2O₃ 9.95 9.95 9.95 9.95 8.94 9.95 B₂O₃ 0.00 0.00 0.00 0.00 0.00 0.00 Li₂O 6.99 7.94 6.98 7.86 7.82 7.82 Na₂O 3.95 4.95 3.95 3.93 4.93 3.97 K₂O 2.94 0.99 2.95 2.95 0.99 2.97 MgO 5.10 5.09 5.16 5.44 6.48 6.29 CaO 2.06 2.06 2.08 1.05 2.10 1.05 SnO₂ 0.10 0.10 0.10 0.10 0.10 0.10 R₂O—Al₂O₃ Li₂O/(R₂O) 0.504 0.572 0.503 0.533 0.569 0.530 Strain Pt. 513.9 521.2 521.3 503.2 502.8 504.1 (° C.) Anneal Pt. 559.4 563.3 564.5 548.8 546.3 548.5 (° C.) Softening Pt. 793.9 770.6 776.6 783.4 766 775.6 (° C.) CTE 70.7 68.6 71.2 71.1 68 71.7 (×10⁻⁷/° C.) Density 2.434 2.465 2.463 2.426 2.436 2.433 (g/cm³) mol % 107WG 107WH 107WI 107WJ 107WK 107WL SiO₂ 67.70 67.24 67.05 66.54 65.01 67.47 Al2O₃ 8.78 8.63 8.46 8.32 7.95 8.57 B₂O₃ 0.00 0.00 0.00 0.00 0.00 0.00 Li₂O 8.78 9.83 10.69 11.72 12.09 8.34 Na₂O 10.89 10.68 10.46 10.33 9.87 10.87 K₂O 0.21 0.17 0.11 0.06 0.27 0.72 MgO 0.83 0.64 0.41 0.21 1.04 1.01 CaO 1.45 1.08 0.72 0.35 1.79 1.63 SnO₂ 0.00 0.00 0.00 0.00 0.00 0.00 R₂O—Al₂O₃ Li₂O/(R₂O) 0.441 0.475 0.503 0.530 0.544 0.418 Strain Pt. 458 457 454 457 444 458 (° C.) Anneal Pt. 499 497 496 497 483 499 (° C.) Softening Pt. 695 691 689 686 664 693 (° C.) CTE 87.6 88.2 89.7 89.3 92.5 89.4 (×10⁻⁷/° C.) Density 2.475 2.482 2.489 2.496 2.502 2.479 (g/cm³) mol % 107WM 107WN 107WO 107WP 107WQ 107WR SiO₂ 67.14 66.58 65.94 66.97 65.95 65.18 Al2O₃ 8.18 7.77 7.40 8.56 8.20 7.83 B₂O₃ 0.00 0.00 0.00 1.37 2.66 3.92 Li₂O 8.47 8.87 9.27 8.15 8.36 8.54 Na₂O 10.76 10.60 10.55 10.52 10.06 9.42 K₂O 1.19 1.63 2.08 0.61 0.93 1.24 MgO 1.02 1.04 1.02 1.22 1.40 1.58 CaO 1.46 1.31 1.15 1.41 1.04 0.69 SnO₂ 0.00 0.00 0.00 0.00 0.00 0.00 R₂O—Al₂O₃ Li₂O/(R₂O) 0.415 0.420 0.423 0.423 0.432 0.445 Strain Pt. 453 449 448 455 452 454 (° C.) Anneal Pt. 493 490 488 493 491 491 (° C.) Softening Pt. 687 680 679 682 665 660 (° C.) CTE 93.6 94 96.1 87.2 87 87.4 (×10⁻⁷/° C.) Density 2.491 2.505 2.517 2.475 2.48 2.485 (g/cm³) mol % 107WS 107WT 107WU 107WV 107WW 107WX SiO₂ 66.97 67.00 67.11 67.13 67.08 67.02 Al2O₃ 9.42 9.45 9.49 9.46 9.49 9.45 B₂O₃ 0.00 0.00 0.00 0.00 0.00 0.00 Li₂O 5.95 5.91 6.80 5.87 6.85 5.85 Na₂O 11.40 11.37 11.90 12.38 11.89 12.43 K₂O 0.26 0.27 0.27 0.26 0.27 0.27 MgO 1.02 3.13 1.55 2.04 1.03 1.04 CaO 3.85 1.78 1.78 1.77 2.29 2.83 SnO₂ 0.10 0.10 0.10 0.10 0.10 0.10 R₂O—Al₂O₃ Li₂O/(R₂O) 0.338 0.337 0.358 0.317 0.360 0.316 Strain Pt. 485 485.4 469.7 476.9 469.5 477.8 (° C.) Anneal Pt. 527.2 528.6 511.9 518.7 511.7 519.5 (° C.) Softening Pt. 728.3 739.8 715.7 726 712.2 720.8 (° C.) CTE (×10⁻⁷/° C.) Density 2.493 2.48 2.479 2.481 2.482 2.488 (g/cm³) mol % 107WY 107WZ 107XA 107XB 107XC 107XD SiO₂ 68.09 68.08 67.11 66.13 65.19 67.16 Al2O₃ 10.05 10.06 10.55 11.04 11.56 11.05 B₂O₃ 0.00 0.00 0.00 0.00 0.00 0.00 Li₂O 7.86 8.78 7.34 7.83 8.22 7.24 Na₂O 9.85 8.87 10.83 10.83 10.84 10.37 K₂O 0.25 0.25 0.25 0.25 0.25 0.25 MgO 1.01 1.03 1.03 1.02 1.03 1.03 CaO 1.78 1.81 1.78 1.79 1.79 1.79 SnO₂ 0.10 0.09 0.10 0.10 0.10 0.10 R₂O—Al₂O₃ Li₂O/(R₂O) 0.438 0.490 0.399 0.414 0.426 0.405 Strain Pt. 481 479 483 483 482 493 (° C.) Anneal Pt. 523 521 526 525 525 536 (° C.) Softening Pt. 736 728 736 731 731 749 (° C.) CTE 83.2 82.2 85.2 84.9 87.3 81.5 (×10⁻⁷/° C.) Density 2.469 2.465 2.476 2.479 2.483 2.473 (g/cm³) mol % 107XE 107XF 107XG 107XH 107XI 107XJ SiO₂ 65.01 64.58 65.20 65.18 64.25 63.48 Al2O₃ 7.26 7.64 6.98 6.97 6.96 6.96 B₂O₃ 0.00 0.00 0.00 0.00 0.00 0.00 Li₂O 10.73 11.72 9.80 9.81 9.81 9.69 Na₂O 9.42 8.46 10.41 10.42 10.42 10.39 K₂O 2.48 2.50 2.50 2.51 2.46 2.45 MgO 0.03 0.03 0.03 0.03 1.03 2.02 CaO 2.06 2.06 2.07 2.07 2.05 2.04 SnO₂ 0.00 0.00 0.00 0.00 0.00 0.00 R₂O—Al₂O₃ Li₂O/(R₂O) 0.474 0.517 0.432 0.431 0.432 0.430 Strain Pt. 451.8 451.7 441.9 433.9 446.9 448.8 (° C.) Anneal Pt. 489.7 491.1 480 470.6 486.5 487.5 (° C.) Softening Pt. 676.4 676.7 653.5 634 673.5 669.7 (° C.) CTE (×10⁻⁷/° C.) Density 2.533 2.53 2.511 2.488 2.543 2.548 (g/cm³) mol % 107XK 107XL 107XM 107XN 107XO 107XP SiO₂ 65.01 64.73 66.60 66.58 65.66 65.04 Al2O₃ 7.29 7.69 9.41 9.45 9.42 9.29 B₂O₃ 0.00 0.00 0.00 0.00 0.00 0.00 Li₂O 10.78 11.68 6.34 6.28 6.34 6.22 Na₂O 9.39 8.41 11.50 11.49 11.46 11.45 K₂O 1.47 1.48 1.23 1.23 1.20 1.22 MgO 0.50 0.49 0.03 0.04 0.98 1.93 CaO 2.56 2.56 2.55 2.54 2.47 2.43 SnO₂ 0.00 0.00 0.00 0.00 0.00 0.00 R₂O—Al₂O₃ Li₂O/(R₂O) 0.498 0.542 0.332 0.331 0.334 0.329 Strain Pt. 456.5 457 478.8 470 488.6 489.5 (° C.) Anneal Pt. 494.9 496.4 519.9 509.2 531.2 532.1 (° C.) Softening Pt. 675.4 677 714.1 690.4 740 737.8 (° C.) CTE (×10⁻⁷/° C.) Density 2.537 2.533 2.497 2.548 2.527 2.533 (g/cm³) mol % 107XQ 107XR 107XS 107XT 107XU 107XV SiO₂ 67.16 66.15 65.20 67.09 66.09 65.07 Al2O₃ 10.07 11.06 12.06 10.06 11.05 12.05 B₂O₃ 0.00 0.00 0.00 0.00 0.00 0.00 Li₂O 7.74 7.71 7.70 8.81 9.76 10.73 Na₂O 10.88 10.88 10.86 9.87 8.88 7.91 K₂O 0.25 0.25 0.25 0.25 0.25 0.25 MgO 0.99 1.03 1.02 1.02 1.04 1.03 CaO 1.79 1.80 1.80 1.78 1.81 1.82 SnO₂ 0.10 0.10 0.10 0.10 0.10 0.10 R₂O—Al₂O₃ Li₂O/(R₂O) 0.410 0.409 0.410 0.465 0.517 0.568 Strain Pt. 475 483 494 473 480 490 (° C.) Anneal Pt. 516 525 536 514 522 532 (° C.) Softening Pt. 722 730 748 715 726 733 (° C.) CTE 86.5 85.3 86.5 85.1 82.9 81.6 (×10⁻⁷/° C.) Density (g/cm³) 2.476 2.473 2.48 2.483 2.474 2.474 mol % 107XW 107XX 107XY 107XZ 107YA 107YB SiO₂ 64.13 65.70 62.52 57.42 63.87 61.20 Al2O₃ 7.57 7.81 6.98 6.61 4.44 4.57 B₂O₃ 0.00 0.00 0.00 0.00 0.00 0.00 Li₂O 11.36 9.48 12.12 18.97 14.62 17.79 Na₂O 10.92 11.26 11.16 10.73 9.51 9.25 K₂O 0.32 0.22 0.24 0.21 0.20 0.22 MgO 1.70 1.56 2.21 1.80 2.01 2.03 CaO 2.40 2.28 2.99 2.80 3.46 3.39 SnO₂ 0.10 0.10 0.10 0.10 0.10 0.10 R₂O—Al₂O₃ Li₂O/(R₂O) 0.503 0.452 0.516 0.634 0.601 0.653 Strain Pt. 439 450 432 406 420 407 (° C.) Anneal Pt. 476 490 469 438 455 441 (° C.) Softening Pt. 645 673 629 570 603 581 (° C.) CTE 108.7 104.3 114.1 101.7 95.1 95.9 (×10⁻⁷/° C.) Density 2.508 2.503 2.524 2.518 2.519 2.515 (g/cm³) mol % 107YC 107YD 107YE 107YF 107YG 107YH SiO₂ 64.66 65.15 65.25 65.22 65.27 65.26 Al2O₃ 10.67 11.20 10.68 9.77 10.68 11.19 B₂O₃ 0.00 0.00 0.00 0.00 0.00 0.00 Li₂O 8.27 7.96 7.93 8.38 7.91 8.34 Na₂O 11.71 11.22 11.18 11.88 11.20 10.73 K₂O 0.27 0.26 0.26 0.28 0.26 0.26 MgO 1.27 1.21 1.21 1.28 1.69 1.21 CaO 1.95 1.88 1.86 1.98 1.86 1.87 SnO₂ 0.10 0.10 0.10 0.10 0.10 0.10 R₂O—Al₂O₃ Li₂O/(R₂O) 0.408 0.409 0.409 0.408 0.408 0.432 Strain Pt. 471.4 479.4 483.9 462.3 476.3 480.4 (° C.) Anneal Pt. 512.2 521.6 526.1 502 518.4 521.8 (° C.) Softening Pt. (° C.) CTE 89.6 87.3 89.7 90.4 87.6 85.8 (×10⁻⁷/° C.) Density 2.491 2.485 2.498 2.49 2.487 2.484 (g/cm³) mol % 107YL 107YN 107YP 107YQ 107YR 107YS SiO₂ 65.99 66.16 65.12 65.15 65.20 65.13 Al2O₃ 9.52 9.54 10.62 10.69 10.69 10.69 B₂O₃ 0.00 0.00 0.00 0.00 0.00 0.00 Li₂O 6.49 6.49 6.15 9.94 7.89 7.98 Na₂O 11.37 11.38 13.18 9.25 10.25 9.25 K₂O 1.24 1.23 0.26 0.26 1.25 2.25 MgO 0.26 0.25 1.70 1.70 1.72 1.70 CaO 2.49 2.51 1.85 1.88 1.87 1.87 SnO₂ 0.09 0.09 0.10 0.10 0.10 0.10 R₂O—Al₂O₃ Li₂O/(R₂O) 0.340 0.340 0.314 0.511 0.407 0.410 Strain Pt. 483 473 474 473 (° C.) Anneal Pt. 525 515 517 515 (° C.) Softening Pt. 0.314 0.511 0.407 0.410 (° C.) CTE (×10⁻⁷/° C.) Density 483 473 474 473 (g/cm³) mol % 107YT 107YU 107YV 107AAC 107AAD 107AAE SiO₂ 64.10 62.85 65.27 67.60 67.52 67.51 Al2O₃ 10.52 10.33 7.93 8.38 8.87 9.35 B₂O₃ 1.89 3.70 0.00 0.00 0.00 0.00 Li₂O 7.65 7.56 8.86 8.03 8.09 8.16 Na₂O 10.96 10.73 10.33 10.72 10.23 9.71 K₂O 0.25 0.24 1.80 0.95 0.95 0.96 MgO 1.68 1.70 0.18 1.05 1.06 1.04 CaO 1.84 1.80 2.73 1.59 1.60 1.59 SnO₂ 0.09 0.09 0.09 0.10 0.09 0.10 R₂O—Al₂O₃ Li₂O/(R₂O) 0.406 0.408 0.422 0.408 0.420 0.434 Strain Pt. 464 466 (° C.) Anneal Pt. 504 503 (° C.) Softening Pt. (° C.) CTE (×10⁻⁷/° C.) Density 2.485 2.482 2.489 2.487 2.485 (g/cm³) mol % 107AAF 107AAG 107AAH 107AAK 107AAL 107AAM SiO₂ 67.45 67.08 67.52 67.73 67.55 67.40 Al2O₃ 8.85 8.87 8.87 8.69 8.63 8.64 B₂O₃ 0.00 0.00 0.00 0.00 0.00 0.00 Li₂O 8.18 8.06 8.59 9.89 10.04 10.20 Na₂O 9.23 10.20 9.71 10.18 10.22 10.22 K₂O 1.96 0.96 0.96 0.31 0.30 0.30 MgO 1.04 1.55 1.05 0.42 0.43 0.42 CaO 1.60 1.60 1.60 0.72 0.73 0.73 SnO₂ 0.10 0.09 0.09 0.00 0.00 0.00 R₂O—Al₂O₃ Li₂O/(R₂O) 0.422 0.419 0.446 0.485 0.488 0.492 Strain Pt. (° C.) Anneal Pt. (° C.) Softening Pt. (° C.) CTE (×10⁻⁷/° C.) Density 2.486 2.49 2.485 (g/cm³) mol % 107AAN 716HZE 716HZJ 716HZQ 716IBA 716IBS SiO₂ 65.67 65.46 65.38 65.45 66.14 65.87 Al2O₃ 10.33 9.40 9.39 9.39 10.30 10.33 B₂O₃ 0.00 0.00 0.00 0.00 0.00 0.00 Li₂O 7.85 6.17 6.13 6.12 7.68 7.71 Na₂O 11.09 11.09 11.12 11.01 10.81 11.01 K₂O 0.76 1.16 1.20 1.17 0.71 0.71 MgO 1.39 2.02 1.99 1.98 1.41 1.42 CaO 1.84 2.40 2.38 2.37 1.81 1.83 SnO₂ 0.00 0.08 0.05 0.05 0.05 0.03 R₂O—Al₂O₃ Li₂O/(R₂O) 0.398 0.335 0.332 0.334 0.400 0.397 Strain Pt. 470 483.2 483.1 487.4 466.5 461.2 (° C.) Anneal Pt. 512 524.9 526.0 529.3 506.8 502.7 (° C.) Softening Pt. 735.4 742.3 711 703.3 (° C.) CTE 87.4 88.7 89.9 89.6 (×10⁻⁷/° C.) Density 2.446 2.532 2.534 2.485 (g/cm³) mol % 716IBT 716IBU 196HLP 196HLQ 196HLR 196HLS SiO₂ 65.92 65.96 60.22 60.03 59.88 59.96 Al2O₃ 10.32 10.32 16.94 14.90 16.84 16.85 B₂O₃ 0.00 0.00 5.83 5.83 5.95 5.92 Li₂O 7.72 7.72 0.00 0.00 4.98 7.00 Na₂O 10.99 10.94 15.85 13.89 11.13 9.07 K₂O 0.70 0.70 1.00 1.00 1.07 1.06 MgO 1.42 1.41 0.02 4.20 0.01 0.02 CaO 1.81 1.81 0.02 0.05 0.02 0.02 SnO₂ 0.03 0.03 0.08 0.08 0.08 0.08 R₂O—Al₂O₃ Li₂O/(R₂O) 0.398 0.399 0.290 0.409 Strain Pt. 461.6 461.3 578.8 559.1 526.2 520.8 (° C.) Anneal Pt. 501.6 502.6 633.6 608.6 577.3 568.4 (° C.) Softening Pt. 702.5 703.1 906 858 820 814 (° C.) CTE 89 90.5 89.6 81.7 85.1 78.7 (×10⁻⁷/° C.) Density 2.406 2.421 2.401 2.395 (g/cm³) mol % 196HLT 196HLU 196HQB 196HQC 196HQD 196HQE SiO₂ 59.87 59.98 60.432 60.351 60.627 60.462 Al2O₃ 15.89 14.88 15.212 16.250 16.612 15.760 B₂O₃ 5.88 5.84 5.949 5.951 5.939 5.928 Li₂O 6.49 5.98 5.860 5.884 6.080 6.995 Na₂O 8.55 7.94 11.391 10.421 9.604 9.665 K₂O 1.05 1.02 0.945 0.935 0.925 0.975 MgO 2.13 4.20 0.045 0.046 0.046 0.046 CaO 0.03 0.05 0.042 0.042 0.045 0.046 SnO₂ 0.08 0.08 0.081 0.081 0.081 0.082 R₂O—Al₂O₃ 0.19 0.06 2.98 0.99 0.00 1.87 Li₂O/(R₂O) 0.403 0.400 0.322 0.341 0.366 0.397 Strain Pt. 509.5 511.6 478.6 486.7 499.3 485.8 (° C.) Anneal Pt. 555.7 557.0 519.0 530.1 544.9 528.1 (° C.) Softening Pt. 784 784 720 775 815 738 (° C.) CTE 76 71 86.7 82.7 80.9 81.5 (×10⁻⁷/° C.) Density 2.406 2.412 2.422 2.407 2.398 2.41 (g/cm³) mol % 196HQF 196HQG 196HQH 196HQI 196HQJ 196HQK SiO₂ 60.462 60.393 60.136 59.979 59.867 60.099 Al2O₃ 14.902 14.918 16.000 16.066 14.972 17.064 B₂O₃ 5.948 5.975 6.079 6.026 8.071 4.087 Li₂O 7.350 5.828 5.851 5.969 5.724 6.228 Na₂O 9.663 9.985 9.753 11.712 10.175 11.295 K₂O 1.450 2.689 1.964 0.028 0.983 0.996 MgO 0.051 0.047 0.045 0.050 0.041 0.052 CaO 0.048 0.043 0.045 0.045 0.043 0.048 SnO₂ 0.084 0.083 0.083 0.083 0.082 0.083 R₂O—Al₂O₃ 3.56 3.58 1.57 1.64 1.91 1.46 Li₂O/(R₂O) 0.398 0.315 0.333 0.337 0.339 0.336 Strain Pt. 470.3 471.0 485.5 491.9 481.0 500.5 (° C.) Anneal Pt. 510.7 510.9 529.4 536.3 523.6 546.1 (° C.) Softening Pt. 701 705 759 756 730 778 (° C.) CTE 85 86.6 84.1 82.2 82.1 88 (×10⁻⁷/° C.) Density 2.42 2.425 2.411 2.413 2.397 2.428 (g/cm³) mol % 196HQL 196HQM 196HVQ 196HVR 196HVS 196HVT SiO₂ 60.140 60.048 60.452 60.473 60.373 62.560 Al2O₃ 16.090 15.056 16.842 16.335 15.823 15.855 B₂O₃ 6.049 6.106 6.039 6.023 6.027 5.918 Li₂O 5.803 5.815 6.683 6.492 6.303 6.325 Na₂O 9.716 9.746 8.751 8.474 8.264 8.148 K₂O 0.982 0.991 0.995 0.992 0.994 0.973 MgO 1.043 2.053 0.055 1.027 2.029 0.047 CaO 0.051 0.059 0.054 0.058 0.061 0.049 SnO₂ 0.082 0.081 0.081 0.079 0.080 0.081 R₂O—Al₂O₃ 0.41 1.50 −0.41 −0.38 −0.26 −0.41 Li₂O/(R₂O) 0.352 0.351 0.407 0.407 0.405 0.409 Strain Pt. 500.8 485.7 (° C.) Anneal Pt. 547.1 529.3 (° C.) Softening Pt. 779 746 (° C.) CTE 81 79.3 (×10⁻⁷/° C.) Density 2.407 2.416 2.395 2.401 2.405 2.385 (g/cm³) mol % 196HVU 196HVV 196HVW 196HVX 196HVY 196HVZ SiO₂ 64.405 62.473 64.869 64.742 64.860 59.773 Al2O₃ 14.859 15.816 13.272 13.276 13.287 14.728 B₂O₃ 5.974 5.973 5.196 5.165 5.151 5.827 Li₂O 5.825 6.272 4.659 5.790 6.667 5.666 Na₂O 7.739 9.220 8.675 7.682 6.689 10.509 K₂O 0.982 0.030 0.026 0.028 0.031 0.028 MgO 0.049 0.047 1.509 1.510 1.499 1.970 CaO 0.045 0.049 0.052 0.055 0.058 0.058 SnO₂ 0.080 0.079 0.006 0.009 0.008 0.005 R₂O—Al₂O₃ −0.31 −0.29 0.09 0.22 0.10 −0.31 Li₂O/(R₂O) 0.400 0.404 0.349 0.429 0.498 0.400 Strain Pt. (° C.) Anneal Pt. (° C.) Softening Pt. (° C.) CTE (×10⁻⁷/° C.) Density 2.375 2.386 2.408 2.406 2.403 2.375 (g/cm³) mol % 196HVZ 196HWA 196HWB 196HXW 196HXX 196HXY SiO₂ 59.773 59.271 58.890 60.00 60.00 60.00 Al2O₃ 14.728 14.635 14.544 16.75 16.25 15.75 B₂O₃ 5.827 5.826 5.797 6.00 6.00 6.00 Li₂O 5.666 5.626 5.587 6.25 6.00 5.75 Na₂O 10.509 10.436 10.325 10.00 9.75 9.50 K₂O 0.028 0.028 0.028 1.00 1.00 1.00 MgO 1.970 1.988 1.960 0.00 1.00 2.00 CaO 0.058 0.061 0.061 SnO₂ 0.005 0.005 0.005 0.08 0.08 0.08 R₂O—Al₂O₃ 1.47 1.46 1.40 0.50 0.50 0.50 Li₂O/(R₂O) 0.350 0.350 0.351 0.362 0.358 0.354 Strain Pt. 496 (° C.) Anneal Pt. 541 (° C.) Softening Pt. 796 (° C.) CTE 81.1 (×10⁻⁷/° C.) Density 2.435 2.446 2.458 2.401 (g/cm³) mol % 196HXZ 196HYA 196HYB SiO₂ 60.00 60.00 62.00 Al2O₃ 16.25 16.75 16.75 B₂O₃ 6.00 6.00 4.00 Li₂O 5.50 6.50 6.25 Na₂O 9.25 10.75 10.00 K₂O 1.00 0.00 1.00 MgO 2.00 0.00 0.00 CaO SnO₂ 0.08 0.08 0.08 R₂O—Al₂O₃ −0.50 0.50 0.50 Li₂O/(R₂O) 0.349 0.377 0.362 Strain Pt. (° C.) Anneal Pt. (° C.) Softening Pt. (° C.) CTE (×10⁻⁷/° C.) Density 2.435 2.446 2.458 (g/cm³)

The lithium aluminosilicate glasses described herein, in some embodiments, may have an elastic modulus of at least about 68 gigaPascals (GPa).

In addition to exemplary compositions of lithium silicate glasses, physical properties, including strain, anneal, and softening points; CTE; and density of these example glasses are listed in Table 2. The strain point was determined using the beam bending viscosity method of ASTM C598-93 (2013). The annealing point was determined using the beam bending viscosity method of ASTM C598-93 (2013). The softening point was determined using the parallel plate viscosity method of ASTM C1351M-96 (2012). The linear coefficient of thermal expansion (CTE) over the temperature range 0-300° C. is expressed in terms of ppm/K and was determined using a push-rod dilatometer in accordance with ASTM E228-11. The density was determined using the buoyancy method of ASTM C693-93 (2013).

In some embodiments, the lithium aluminosilicate glasses described herein have a liquidus viscosity of greater than about 10,000 Poise (P) and, in certain embodiments, greater than 100,000 P. In some embodiments, these glasses are compatible with fusion processes, such as fusion draw processes or the like, and compatible with zircon hardware used in forming. However, in some embodiments (e.g., example 3 in Table 1) these glasses have low liquidus viscosities and are therefore not fusion-formable. In these instances, the glass may be formed by slot draw, float, rolling, and other sheet-forming processes known in the art.

The glasses described herein may be formed into articles such as, but not limited to, flat plates and three dimensional articles having thicknesses ranging from about 0.2 mm up to about 2 mm and, in some embodiments, from about 0.5 mm to about 1.5 mm.

The viscosity and mechanical performance are influenced by glass compositions. In the glass compositions described herein, SiO₂ serves as the primary glass-forming oxide and can serve to stabilize the networking structure. The concentration of SiO₂ should be sufficiently high in order to provide the glass with sufficiently high chemical durability suitable for consumer applications. However, the melting temperature (200 poise temperature) of pure SiO₂ or high content SiO₂ glasses is too high to allow the glass to be processed by certain methods. Furthermore, the presence of SiO₂ decreases the compressive stress created by ion exchange. In some embodiments, the lithium aluminosilicate glasses described herein comprise from about 55 mol % to about 75 mol % SiO₂, such as from about 57 mol % to about 73 mol % SiO₂; from about 59 mol % to about 71 mol % SiO₂; from about 61 mol % to about 69 mol % SiO₂; from about 63 mol % to about 67 mol % SiO₂; from about 55 mol % to about 60 mol % SiO₂; from about 58 mol % to about 69 mol % SiO₂; or any sub-ranges contained therein.

Al₂O₃ may also serve as a glass former in these glasses. Like SiO₂, alumina generally increases the viscosity of the melt, and an increase in Al₂O₃ relative to the alkalis or alkaline earths generally results in improved durability. The structural role of the aluminum ions depends on the glass composition. When the concentration of alkali metal oxides (R₂O) is close to or greater than the concentration of alumina (Al₂O₃), all aluminum is found in tetrahedral coordination with the alkali metal ions acting as charge-balancers. This is the case for all of the glasses described herein. In general, Al₂O₃ also plays an important role in ion exchangeable glasses, as it enables a strong network backbone (i.e., high strain point) while allowing for the relatively fast diffusivity of alkali ions. However, high Al₂O₃ concentrations generally lower the liquidus viscosity and thus Al₂O₃ concentration needs to be controlled in a reasonable range. In some embodiments, the glasses described herein comprise from about 9 mol % to about 18 mol % Al₂O₃, such as from about 10 mol % to about 18 mol % Al₂O₃; from about 12 mol % to about 16 mol % Al₂O₃; from about 12 mol % to about 15 mol % Al₂O₃; from about 9 mol % to about 17 mol % Al₂O₃; or any sub-ranges contained therein.

Alkali oxides (Li₂O, Na₂O, K₂O, Rb₂O, and Cs₂O) serve as aids in achieving low melting temperature and low liquidus temperatures. On the other hand, the addition of alkali oxide dramatically increases the coefficient of thermal expansion (CTE) and lowers the chemical durability. Most importantly, to perform ion exchange, the presence of at least one small alkali oxide such as Li₂O and Na₂O is required to exchange with larger alkali ions (e.g., K⁺) from an ion exchange medium, such as a salt bath. Three types of ion exchange can generally be carried out: Na⁺-for-Li⁺ exchange, which results in a deep depth of layer but low compressive stress; K⁺-for-Li⁺ exchange, which results in a small depth of layer but a relatively large compressive stress; and K⁺-for-Na⁺ exchange, which results in intermediate depth of layer and compressive stress. Because compressive stress is proportional to the number of alkali ions that are exchanged out of the glass, a sufficiently high concentration of the at least one small alkali oxide is needed to produce a large compressive stress in the glass. In some embodiments, the glasses described herein comprise from about 2.5 mol % to about 20 mol % Li₂O, such as from about 3 mol % to about 20 mol % Li₂O; from about 4 mol % to about 18 mol % Li₂O; from about 5 mol % to about 16 mol % Li₂O; from about 6 mol % to about 14 mol % Li₂O; from about 5 mol % to about 14 mol % Li₂O; from about 7 mol % to about 10 mol % Li₂O; from about 2.5 mol % to about 12 mol % Li₂O; from about 4 mol % to about 10 mol % Li₂O; or any sub-ranges contained therein. In some embodiments, these glasses comprise from 0 mol % to about 14 mol % Na₂O; such as from 0 mol % to about 5 mol % Na₂O; from about 0.2 mol % to about 12 mol % Na₂O; from about 4 mol % to about 14 mol % Na₂O; from 0.2 mol % to about 14 mol % Na₂O; or any sub-ranges contained therein. The glasses described herein, in some embodiments, may comprise from 0 mol % to about 4 mol % K₂O, such as from 0 mol % to about 2.5 mol % K₂O; from 0 mol % to about 1 mol % K₂O; or any sub-ranges contained therein.

To achieve a high liquidus viscosity and thus make formation by down-draw techniques, particularly by the fusion draw method, Li₂O glass should account for less than half of the total alkali oxide content on a molar basis. When Li₂O/(Li₂O+Na₂O+K₂O+Rb₂O+Cs₂O) exceeds 0.5, the spodumene liquidus increases and the glasses are no longer compatible with the fusion technique. Thus, in some embodiments, Li₂O/(Li₂O+Na₂O+K₂O+Rb₂O+Cs₂O) is in a range from about 0.1 to about 0.5; such as 0.1≤Li₂O/(Li₂O+Na₂O+K₂O+Rb₂O+Cs₂O)≤0.4, 0.2≤Li₂O/(Li₂O+Na₂O+K₂O+Rb₂O+Cs₂O)≤0.4, or any sub-ranges contained therein. To achieve high compressive stress at depth after ion exchange, however, it is desirable to maximize the Li₂O content. To achieve a compressive stress of greater than 100 MPa at depths greater than 40 um, the Li₂O content should therefore be greater than about 4 mol % and, in some embodiments, preferably greater than about 5 mol %, and should be less than about 10 mole %.

The presence of K₂O increases the rate of K⁺ for Na⁺ ion exchange but drastically decreases the compressive stress after ion exchange. In some embodiments, the glass should comprise less than about 2.5 mol % K₂O and, in certain embodiments, the K₂O concentration should not exceed 1 mole %.

Divalent cation oxides (such as alkaline earth oxides and zinc oxide) also improve the melting behavior of the glass. With respect to ion exchange performance, however, the presence of divalent cations acts to decrease alkali cation mobility. This negative effect on ion exchange performance is especially pronounced with the larger divalent cations. Furthermore, the smaller divalent cation oxides generally help enhance the compressive stress more than the larger divalent cation oxides. Hence, MgO offers several advantages with respect to improved stress relaxation while minimizing the adverse effects on alkali diffusivity. However, when the contents of MgO are high, the glasses are prone to form forsterite (Mg₂SiO₄), which causes the liquidus temperature to rise very steeply as MgO concentration rises above a certain level. In some embodiments, MgO is the only divalent cation oxide present in the glass. In other embodiments, the glasses described herein may contain at least one of MgO and ZnO. Accordingly, these glasses, in some embodiments, may comprise from 0 mol % to about 8 mol % MgO, such as from 0 mol % to about 6 mol % MgO; from 0 mol % to about 5 mol % MgO; from 0 mol % to about 3 mol % MgO; from 0 mol % to about 1 mol % MgO; or any sub-ranges contained therein. In some embodiments, the glass may comprise from 0 mol % to about 4 mol % ZnO, such as from 0 mol % to about 3 mol % ZnO; from 0 mol % to about 2 mol % ZnO; from 0 mol % to about 1 mol % ZnO, or any sub-ranges contained therein.

When boron is not charge balanced by alkali oxides or divalent cation oxides, it will be in a trigonal coordination state, and thus open up the glass structure. The network around the trigonally coordinated boron is not as rigid as those surrounding tetrahedrally coordinated boron; the bonds are “floppy (i.e. elastic, flexible, or capable of bending or stretching)” and therefore allow the glasses to tolerate some deformation before crack formation. Furthermore, boron decreases the melting viscosity and effectively helps suppress the zircon breakdown viscosity of the glass. In some embodiments, the glasses described herein contain from 0 mol % to about 20 mol % B₂O₃, such as from about 2.5 mol % to about 20 mol % B₂O₃; from about 3 mol % to about 18 mol % B₂O₃; from about 3.5 mol % to about 16 mol % B₂O₃; from about 4 mol % to about 16 mol % B₂O₃; from about 4.5 mol % to about 14 mol % B₂O₃; from about 5 mol % to about 12 mol % B₂O₃; from about 2.5 mol % to about 7.5 mol % B₂O₃; from about 5 mol % to about 7 mol % B₂O₃; from about 3.5 mol % to about 9.5 mol % B₂O₃; from about 5 mol % to about 9 mol % B₂O₃; or any sub-ranges contained therein.

P₂O₅ improves damage resistance and does not impede ion exchange. In some embodiments, the addition of phosphorous to the glass creates a structure in which silica (SiO₂ in the glass) is replaced by aluminum phosphate (AlPO₄), which consists of tetrahedrally coordinated aluminum and phosphorus and/or boron phosphate (BPO₄), which consists of tetrahedrally coordinated boron and phosphorus. In some embodiments, the glass comprises from 0 to about 4 mol % P₂O₅, such as from 0 mol % to about 3 mol % P₂O₅; from 0 mol % to about 2.5 mol % P₂O₅; from 0 mol % to about 1 mol % P₂O₅; or any sub-ranges contained therein.

TiO₂ serves as a nucleation agent to produce bulk nucleation if a glass-ceramic article is desired. If the concentration of TiO₂ is too low, the precursor glass does not crystallize. If the concentration is too high, the devitrification, upon cooling during precursor glass forming, can be difficult to control. In some embodiments, the glasses described herein may comprise from 0 mol % to about 5 mol % TiO₂, such as from 0 mol % to about 4 mol % TiO₂; from 0 mol % to about 3 mol % TiO₂; from 0 mol % to about 2 mol % TiO₂; from 0 mol % to about 1 mol % TiO₂; or any sub-ranges contained therein.

In some embodiments, the glasses described herein may further include at least one fining agent such as, but not limited to, SnO₂, As₂O₃, Sb₂O₃, and the like. Due to environmental and toxicity concerns, As₂O₃ and Sb₂O₃ are typically not included in glasses. Accordingly, the glasses described herein are typically free of As₂O₃ and Sb₂O₃ and, in some embodiments, these glasses may comprise from about 0.05 mol % to about 0.5 mol % SnO₂.

Rare earth oxides may increase the hardness and elastic modulus of a glass, but they hamper ion exchange, increase the density and cost of the glass, and many impart color to the glass. It is therefore desirable to limit the total rare earth oxide content to less than 0.1 mol %.

In some aspects, the lithium aluminosilicate glasses described herein are strengthened by forming a compressive layer on the surfaces of the glass. In certain embodiments, these glasses are chemically strengthened, and in particular embodiments, are chemically strengthened by ion exchange.

Ion exchange is a process in which smaller cations in the glass are exchanged for larger cations that are present in an ion exchange medium such as a molten salt bath or a paste. In a particular embodiment, ion exchange is carried out by immersing the glass in a molten salt bath substantially comprising a salt of the larger cation. The ion exchange bath may also comprise salts of the smaller cations that are present in the glass. As used herein, the term “substantially comprising” means that other components may be present in the molten salt bath. Such components may include, but are not limited to, compounds that act to reduce attack of the bath vessel or the glass article by the molten salt. Such additional components may include, but are not limited to, selected components of the glass, such as silicic acid, alumina in gel form, silica in gel form, or the like.

A cross-sectional schematic view of an ion exchanged glass article is shown in FIG. 1 . Glass article 100 has a thickness t, first surface 110, and second surface 112. Glass article 100, in some embodiments, has a thickness t of up to about 1 mm. While the embodiment shown in FIG. 1 depicts glass article 100 as a flat planar sheet or plate, glass article may have other configurations, such as three dimensional shapes or non-planar configurations. Glass article 100 has a first compressive layer 120 extending from first surface 110 to a depth of layer (DOL) d₁ into the bulk of the glass article 100. In the embodiment shown in FIG. 1 , glass article 100 also has a second compressive layer 122 extending from second surface 112 to a second depth of layer d₂. First and second compressive layers 120, 122 are each under a compressive stress CS. In some embodiments, first and second compressive layers 120, 122 each have a maximum compressive stress at the first and second surfaces 110, 112, respectively. Glass article also has a central region 130 that extends from d₁ to d₂. Central region 130 is under a tensile stress or central tension (CT), which balances or counteracts the compressive stresses of layers 120 and 122. The depths of layer d₁, d₂ of first and second compressive layers 120, 122 protects the glass article 100 from the propagation of flaws introduced by sharp impact to first and second surfaces 110, 112 of glass article 100, while the compressive stress of at least about 900 MPa minimizes the likelihood of a flaw penetrating through the depth d₁, d₂ of first and second compressive layers 120, 122.

When ion exchanged, the lithium aluminosilicate glasses described herein typically exhibit, relative to their sodium analogs, deep depths of layer and low central tension, thus enabling very thin (i.e., <0.5 mm) sheets of glass to be chemically strengthened while not being susceptible to frangible behavior.

Compressive stress (including surface CS) is measured by surface stress meter (FSM) using commercially available instruments such as the FSM-6000, manufactured by Orihara Industrial Co., Ltd. (Japan). Surface stress measurements rely upon the accurate measurement of the stress optical coefficient (SOC), which is related to the birefringence of the glass. SOC in turn is measured according to Procedure C (Glass Disc Method) described in ASTM standard C770-16, entitled “Standard Test Method for Measurement of Glass Stress-Optical Coefficient,” the contents of which are incorporated herein by reference in their entirety.

As used herein, DOL means the depth at which the stress in the chemically strengthened alkali aluminosilicate glass article described herein changes from compressive to tensile. DOL may be measured by FSM or a scattered light polariscope (SCALP) depending on the ion exchange treatment. Where the stress in the glass article is generated by exchanging potassium ions into the glass article, FSM is used to measure DOL. Where the stress is generated by exchanging sodium ions into the glass article, SCALP is used to measure DOL. Where the stress in the glass article is generated by exchanging both potassium and sodium ions into the glass, the DOL is measured by SCALP, since it is believed the exchange depth of Na⁺ ions (“Potassium DOL”) indicates the DOL and the exchange depth of potassium ions indicates a change in the magnitude of the compressive stress (but not the change in stress from compressive to tensile). The depth of penetration of K⁺ ions (“Potassium DOL”) represents the depth of potassium penetration as a result of an ion exchange process. The Potassium DOL is typically less than the DOL for the articles described herein. Potassium DOL is measured using a surface stress meter such as the commercially available FSM-6000 surface stress meter, manufactured by Luceo Co., Ltd. (Tokyo, Japan), which relies on accurate measurement of the stress optical coefficient (SOC), as described above with reference to the CS measurement.

The lithium aluminosilicate glasses described herein may be subjected to an ion exchange process in at least one molten salt bath containing either sodium salts, potassium salts, or both sodium and potassium salts. The nitrate salts NaNO₃ and KNO₃ are typically used in the ion exchange process. The glasses are held in a salt bath for a time sufficient for ion exchange to occur on the surface and into some depth into the article. In one embodiment, the glass is chemically strengthened by immersion in a molten salt bath comprising NaNO₃ for a predetermined time period to achieve a desired level of ion exchange. As a result of the ion exchange, a surface compressive layer is created caused by the substitution of Li⁺ ions contained in a glass surface layer by Na⁺ or K⁺ ions, both of which have a larger ionic radius than Li⁺. In one embodiment, the temperature of the molten salt bath is about 390° C. and the predetermined time period is in a range from about one to four hours. In other embodiments, ion exchange is carried out in at least one molten salt bath at temperatures ranging from about 370° C. to about 390° C.

In some embodiments, the glasses described herein may undergo ion exchange with monovalent silver cations, thus providing the glass surface with antimicrobial properties. Since the ionic radius of Ag⁺ is greater than that of either Li⁺ or Na⁺, silver ion exchange of these glasses results in a lower loss of compressive stress than observed in ion exchanged glasses that contain only sodium and potassium.

In some embodiments, the lithium aluminosilicate glasses described herein may be ion exchanged to achieve a depth of layer of at least about 70 μm when ion exchanged for periods of less than about 7 hours. In addition, these glasses may be ion exchanged to achieve maximum compressive stresses at the surface of the glass of at least about 500 MPa in a one-step ion exchange process, or at least about 600 MPa in a two-step ion exchange process, with some glasses achieving maximum compressive stresses as high as 840 MPa in a one-step ion exchange and as high as 1000 MPa at the glass surface in a two-step ion exchange process. In some embodiments, a compressive stress of at least 700 MPa, or at least about 800 MPa, or at least about 900 MPa may be achieved using either a one-step or a two-step ion exchange process. In some embodiments, the compressive stress in these ion exchanged glasses may be about 50 MPa or greater at depths of 100 μm or more below the surface.

The lithium aluminosilicate glasses described herein may be ion exchanged to achieve depths of compressive layer of at least about 70 μm; in some embodiment, at least about 100 μm; and in still other embodiment, at least about 150 μm by either one-step or two-step ion exchange processes. The ion exchange time at temperatures ranging 370° C. to about 390° C. needed to achieve these depths of layer by either a one-step or two-step process is less than about 7 hours.

The profile and depth of the compressive layer may be determined from the concentration profile of the larger cations participating in the ion exchange process. The Na⁺ concentration profile from the surface of the glass to the inner portion of a 1) lithium aluminosilicate glass (example 3 in Table 1) and a glass ceramic (Corning Code 9667; nominal composition listed in Table 1) that had been cerammed at 975° C. for 4 hours) that were ion exchanged at 390° C. for 3.5 hours in a NaNO₃ molten salt bath are shown in FIG. 2 . In some embodiments, a depth of layer DOL of at least 100 μm, determined from the Na₂O concentration profile, may be achieved for the lithium aluminosilicate glass (1 in FIG. 2 ).

Table 3 lists conditions for one-step ion exchange, CS, depth of K⁺ penetration into the glass, and depth of Na⁺ penetration into the glass for compositions selected from Table 2. Two-step ion exchange conditions, fictive temperature T_(f), CS, and DOL for compositions selected from Table 2 are listed in Table 4.

TABLE 3 One-step ion exchange conditions, compressive stress (CS), and K⁺ and Na⁺ penetration for compositions selected from Table 2. 196HLP 196HLQ 196HLR 196HLS 196HLT 196HLU Ion exchange in 100 wt % KNO₃ at 430° C. for 2 hours CS (MPa) 998 861 876 860 905 881 K⁺ DOL (μm) 40 25 22 19 14 11 Ion exchange in 90 wt % KNO₃/10 wt % NaNO₃ at 390° C. for 3 hours CS (MPa) 637 581 683 701 728 667 K⁺ DOL (μm) 29.6 17.5 13.6 10.1 8.2 7.5 Na⁺ DOL (μm) 244 267 237 247 Ion exchange in 80 wt % KNO₃/20 wt % NaNO₃ at 390° C. for 3 hours CS (MPa) 512 460 606 658 633 651 K⁺ DOL (μm) 29.0 16.3 13.5 9.8 7.3 7.9 Na⁺ DOL (μm) 280 273 237 224 Ion exchange in 60 wt % KNO₃/40 wt % NaNO₃ at 390° C. for 3 hours CS (MPa) 348 302 505 542 K⁺ DOL (μm) 26.9 15.7 12.6 8.7 Na⁺ DOL (μm) 244 293 198 195 Ion exchange in 100 wt % NaNO₃ at 370° C. for 0.75 hour CS (MPa) Na⁺ DOL (μm) 198 182 185 192 196HQB 196HQC 196HQD 196HQE 196HQF 196HQG Ion exchange in 95 wt % KNO_(3/5) wt % NaNO₃ at 390° C. for 3 hours CS (MPa) 722 780 822 779 721 651 K⁺ DOL (μm) 8.3 9.8 10.7 7.9 7.1 10.4 Na⁺ DOL (μm) 215 221 228 202 215 182 Ion exchange in 90 wt % KNO₃/10 wt % NaNO₃ at 390° C. for 3 hours CS (MPa) 670 693 741 695 695 582 K⁺ DOL (μm) 7.8 9.9 10.1 7.4 6.9 10.9 Na⁺ DOL (μm) 224 228 250 224 234 195 Ion exchange in 80 wt % KNO₃/20 wt % NaNO₃ at 390° C. for 3 hours CS (MPa) 568 604 639 599 579 486 K⁺ DOL (μm) 7.6 9.8 10.0 7.5 7.1 8.9 Na⁺ DOL (μm) 202 241 208 244 231 205 Ion exchange in 100 wt % NaNO₃ at 370° C. for 0.75 hour CS (MPa) Na⁺ DOL (μm) 189 192 179 176 182 182 196HQH 196HQI 196HQJ 196HQK 196HQL 196HQM Ion exchange in 95 wt % KNO_(3/5) wt % NaNO₃ at 390° C. for 3 hours CS (MPa) 713 789 707 848 822 766 K⁺ DOL (μm) 11.2 7.7 9.9 10.2 8.8 7.0 Na⁺ DOL (μm) 182 241 202 250 228 224 Ion exchange in 80 wt % KNO₃/20 wt % NaNO₃ at 390° C. for 3 hours CS (MPa) 539 629 613 652 611 602 K⁺ DOL (μm) 10.5 5.4 5.3 9.1 8.1 7.2 Na⁺ DOL (μm) 192 254 202 257 234 195 Ion exchange in 60 wt % KNO₃/40 wt % NaNO₃ at 390° C. for 3 hours CS (MPa) 455 503 460 528 510 485 K⁺ DOL (μm) 9.6 7.4 8.1 8.8 8.3 7.6 Na⁺ DOL (μm) 205 260 185 244 237 205 Ion exchange in 100 wt % NaNO₃ at 370° C. for 0.75 hour CS (MPa) Na⁺ DOL (μm) 172 169 169 169 172 172

TABLE 4 Two-step ion exchange conditions, fictive temperature T_(f), CS, and DOL for compositions selected from Table 2. 196HLR 196HLS 196HLT 196HLU T_(f) (° C.) 652 638 623 623 Bath 1 Temperature 390 390 390 390 (° C.) Time (hr) 0.75 0.75 0.75 0.75 Composition 80% KNO₃ 80% KNO₃ 80% KNO₃ 80% KNO₃ (wt %) 20% NaNO₃ 20% NaNO₃ 20% NaNO₃ 20% NaNO₃ Bath 2 Temperature 390 390 390 390 (° C.) Time (hr) 0.75 0.75 0.75 0.75 Composition 100% KNO₃ 100% KNO₃ 100% KNO₃ 100% KNO₃ (wt %) CS (MPa) 1041 1068 1042 DOL (μm) 185 195 163 195

Vickers crack initiation thresholds described herein are determined by applying and then removing an indentation load to the glass surface at a rate of 0.2 mm/min. The maximum indentation load is held for 10 seconds. The indentation cracking threshold is defined at the indentation load at which 50% of 10 indents exhibit any number of radial/median cracks emanating from the corners of the indent impression. The maximum load is increased until the threshold is met for a given glass composition. All indentation measurements are performed at room temperature in 50% relative humidity. The test involved the use of a square-based pyramidal diamond indenter with an angle of 136° between faces, referred to as a Vickers indenter. The Vickers indenter was same as the one used in standard micro hardness testing (reference ASTM-E384-11).

As used herein, the term “Knoop Scratch Threshold” refers to the onset of lateral cracking. In Knoop threshold testing, a mechanical tester holds a Knoop diamond in which a glass is scratched at increasing loads to determine the onset of lateral cracking. As used herein, Knoop Scratch Threshold is the onset of lateral cracking (in 3 or more of 5 indentation events). In Knoop Scratch Lateral Cracking Threshold testing, samples of the glass articles and articles were first scratched with a Knoop indenter under a dynamic or ramped load to identify the lateral crack onset load range for the sample population. Once the applicable load range is identified, a series of increasing constant load scratches (3 minimum or more per load) are performed to identify the Knoop scratch threshold. The Knoop scratch threshold range can be determined by comparing the test specimen to one of the following 3 failure modes: 1) sustained lateral surface cracks that are more than two times the width of the groove, 2) damage is contained within the groove, but there are lateral surface cracks that are less than two times the width of groove and there is damage visible by naked eye, or 3) the presence of large subsurface lateral cracks which are greater than two times the width of groove and/or there is a median crack at the vertex of the scratch.

When ion exchanged in NaNO₃, the glasses described herein exhibit high native damage resistance, and, in some embodiments, capable of achieving a Vickers crack initiation threshold of over 50 kilogram force (kgf). This level of damage resistance may be achieved, for example, for the glasses described herein containing 6 mol % Li₂O following ion exchange at 390° C. in a NaNO₃ bath for 3.5 hours. This Vickers crack initiation threshold value is comparable to—or greater than—those exhibited by analogous sodium aluminosilicate glasses having high levels of inherent damage resistance. FIG. 3 is a plot of indentation fracture thresholds (IFT) determined after ion exchange in KNO₃ for the present lithium aluminosilicate glass (example 3 in Table 1, ion exchanged at 390° C. in NaNO₃ for 3.5 hours) (C in FIG. 3 ), and in fusion-formed sodium aluminosilicate glasses A and E (nominal composition: 67.6 mol % SiO₂; 3.7 mol % B₂O3; 12.7 mol % Al₂O₃; 13.7 mol % Na₂O; 0.01 mol % K₂O; 2.3 mol % MgO; and 0.1 mol % SnO₂) with IFT of 15-20 kgf; glass B (nominal composition: 64.7 mol % SiO₂; 5.1 mol % B₂O3; 13.9 mol % Al₂O₃; 13.7 mol % Na₂O; 2.4 mol % MgO; and 0.08 mol % SnO₂) with IFT of 30-40 kgf; and glass D (nominal composition: 64.7 mol % SiO₂; 5.1 mol % B₂O3; 13.9 mol % Al₂O₃; 13.7 mol % Na₂O; 2.4 mol % MgO; and 0.08 mol % SnO₂) with IFT of 15 kgf Optical microscopic images of Vickers indentations in the ion exchanged lithium aluminosilicate glass plotted in FIG. 3 under indenter loads of 10 kgf (a in FIG. 4 ), 30 kgf (b), and 50 kgf (c) are shown in FIG. 4 . The images in FIG. 4 show significant glass densification without formation of lateral cracking, indicating that the glass possesses a high level of inherent damage resistance.

In some embodiments, the glasses described herein, when ion exchanged as detailed above, may exhibit Vickers crack initiation thresholds (VIT) of at least 10 kgf; in some embodiments, at least 15 kgf; and in still other embodiments, at least about 20 kgf. In certain embodiments, the Vickers crack initiation threshold is in a range from about 10 kgf to about 35 kgf and Knoop scratch thresholds (KST) are in a range from about 10 Newtons (N) to about 20 N.

Vickers crack initiation thresholds (VIT) and Knoop scratch thresholds (KST) for glasses that were ion exchanged in one-step and two-step ion exchange processes are listed in Tables 3 and 4, respectively.

The articles disclosed herein may be incorporated into another article such as an article with a display (or display articles) (e.g., consumer electronics, including mobile phones, tablets, computers, navigation systems, and the like), architectural articles, transportation articles (e.g., automotive, trains, aircraft, sea craft, etc.), appliance articles, or any article that requires some transparency, scratch-resistance, abrasion resistance or a combination thereof. An exemplary article incorporating any of the strengthened articles disclosed herein is shown in FIGS. 5A and 5B. Specifically, FIGS. 5A and 5B show a consumer electronic device 200 including a housing 202 having front 204, back 206, and side surfaces 208; electrical components (not shown) that are at least partially inside or entirely within the housing and including at least a controller, a memory, and a display 210 at or adjacent to the front surface of the housing; and a cover substrate 212 at or over the front surface of the housing such that it is over the display. In some embodiments, the cover substrate 212 and/or housing may include any of the strengthened articles disclosed herein.

While typical embodiments have been set forth for the purpose of illustration, the foregoing description should not be deemed to be a limitation on the scope of the disclosure or appended claims. Accordingly, various modifications, adaptations, and alternatives may occur to one skilled in the art without departing from the spirit and scope of the present disclosure and appended claims. 

1. A lithium aluminosilicate glass article, wherein the lithium aluminosilicate glass article is formed from a glass comprising: from 55 mol % to 75 mol % SiO₂; from 10 mol % to 18 mol % Al₂O₃; from 6 mol % to 14 mol % Li₂O; from 2.5 mol % to 9.5 mol % B₂O₃; and from 0 mol % to 4 mol % P₂O₅.
 2. The lithium aluminosilicate glass article of claim 1, wherein the glass comprises: from 57 mol % to 67 mol % SiO₂.
 3. The lithium aluminosilicate glass article of claim 1, wherein the glass comprises: from 12 mol % to 18 mol % Al₂O₃.
 4. The lithium aluminosilicate glass article of claim 1, wherein the glass comprises: from 6 mol % to 12.6 mol % Li₂O.
 5. The lithium aluminosilicate glass article of claim 1, wherein the glass comprises: from 3 mol % to 7.5 mol % B₂O₃.
 6. The lithium aluminosilicate glass article of claim 1, wherein the glass comprises: from 3.5 mol % to 7 mol % B₂O₃.
 7. The lithium aluminosilicate glass article of claim 1, wherein the glass comprises: from 0 mol % to 3 mol % P₂O₅.
 8. The lithium aluminosilicate glass article of claim 1, wherein the glass comprises: from 0 mol % to 2.5 mol % P₂O₅.
 9. The lithium aluminosilicate glass article of claim 1, wherein the glass comprises: from 0 mol % to 4 mol % K₂O.
 10. The lithium aluminosilicate glass article of claim 1, wherein the glass comprises: from 0 mol % to 1 mol % K₂O.
 11. The lithium aluminosilicate glass article of claim 1, wherein the glass from which the lithium aluminosilicate glass article is formed has a liquidus viscosity of at least 10 kP.
 12. The lithium aluminosilicate glass article of claim 1, wherein the lithium aluminosilicate glass has a softening point of 840° C. or less.
 13. The lithium aluminosilicate glass article of claim 1, wherein the glass from which the lithium aluminosilicate glass article is formed has an anneal point of at least 510° C.
 14. The lithium aluminosilicate glass article of claim 1, wherein the glass from which the lithium aluminosilicate glass article is formed has an elastic modulus of at least 68 GPa.
 15. The lithium aluminosilicate glass article of claim 1, wherein the glass from which the lithium aluminosilicate glass article is formed is characterized by (Al₂O₃ (mol %)+B₂O₃ (mol %))/R₂O (mol %) is in a range from 0.9 to 1.9, where and R₂O=Li₂O+Na₂O+K₂O+Rb₂O+Cs₂O.
 16. The lithium aluminosilicate glass article of claim 1, wherein the glass is characterized by Al₂O₃ (mol %)>B₂O₃ (mol %).
 17. The lithium aluminosilicate glass of claim 1, wherein the glass comprises: from 0 mol % to 1 mol % TiO₂.
 18. The lithium aluminosilicate glass of claim 1, wherein the glass comprises: from 0 mol % to 2 mol % ZnO.
 19. The lithium aluminosilicate glass of claim 1, wherein the glass is free of As₂O₃ and Sb₂O₃.
 20. A consumer electronic product, comprising: a housing having a front surface, a back surface and side surfaces; electrical components provided at least partially within the housing, the electrical components including at least a controller, a memory, and a display, the display being provided at or adjacent the front surface of the housing; and a cover glass disposed over the display, wherein at least one of a portion of the housing or the cover glass comprises the lithium aluminosilicate glass article of claim
 1. 